Strain Age Embrittlement

استعرض الموضوع السابق استعرض الموضوع التالي اذهب الى الأسفل

Strain Age Embrittlement

مُساهمة من طرف Admin في الإثنين مارس 24, 2008 2:05 am

Strain Age Embrittlement

This phenomenon applies to carbon and low alloy steel. It involves ferrite forming a compound with nitrogen; iron-nitride (Fe4N). Temperatures around 250°C, will cause a fine precipitation of this compound to occur. It will tend to pin any dislocations in the structure that have been created by cold work or plastic deformation.


Strain ageing increases tensile strength but significantly reduces ductility and toughness.

Modern steels tend to have low nitrogen content, but this is not necessarily true for welds. Sufficient Nitrogen, approximately 1 to 2 ppm, can be easily picked up from the atmosphere during welding.

Weld root runs are particularly at risk because of high contraction stresses causing plastic deformation. This is why impact test specimens taken from the root or first pass of a weld can give poor results.
Additions of Aluminium can tie up the Nitrogen as Aluminium Nitride, but weld-cooling rates are too fast for this compound to form successfully. Stress relief at around 650 degrees C will resolve the problem.

Admin
المدير العام
المدير العام

عدد الرسائل : 323
العمر : 34
تاريخ التسجيل : 05/09/2007

معاينة صفحة البيانات الشخصي للعضو http://gewc.ahlamontada.com/

الرجوع الى أعلى الصفحة اذهب الى الأسفل

رد: Strain Age Embrittlement

مُساهمة من طرف ENG_3ALIM في السبت مارس 29, 2008 9:26 pm

جزاك الله خير على المعلومات القيمه

ومستنين منك المزيد

ENG_3ALIM
مشرف تكنولوجيا اللحام
مشرف تكنولوجيا اللحام

عدد الرسائل : 56
العمر : 30
تاريخ التسجيل : 08/03/2008

معاينة صفحة البيانات الشخصي للعضو

الرجوع الى أعلى الصفحة اذهب الى الأسفل

استعرض الموضوع السابق استعرض الموضوع التالي الرجوع الى أعلى الصفحة


 
صلاحيات هذا المنتدى:
لاتستطيع الرد على المواضيع في هذا المنتدى